Stainless Steel Electrodes

ES 410 B A5.4: E 410-15 / EN 1600: E 13 B 22

Description

ES 410 B It is a basic coated electrode. % 13 Cr used in joint and filling welding of martensitic and martensitic-ferritic steels with 13 % Cr and steel casts. This electrode is also stronge at filling in the surfaces of gas, water and stream armatures. Electrodes should be dried for 2 hours at 150°C-200°C before use., Annealing at 750°C for 2 hours, cooling down to room temperature in the furnace re-drying at 150 °C - 200 °C /min.

Typical Chemical Composition (%)

SiMnCrC
0.70.813.50.07

Typical Mechanical Properties

Yeild Strength Tensile Strength Elongation 5x D Impact (ISO-V)
450 - 500 N / mm² 650 - 800 N / mm² % 20 | As weld | 750ºC/2 h/furnace| ~350 HB | 200 HB

Applications

Sizes Available & Recomennded Currents

Diam. (mm) Length (mm) Current (Amperes) Arc Voltage Wire Feed
2.5 250 50 - 90
3.20 350 80 - 120
4.00 350 110 - 160

Welding Current

DC ( + )

Welding Positions


Flat

Horizontal

Vertical Up
 
Overhead

Fillet

Hardness (HB)


Special Coating ( performs several functions)


Typical Base Material Grades